超高分子管道生產(chǎn)規(guī)格
閱讀：244 發(fā)布時(shí)間：2017-5-16直徑 | 0.6MPa | 0.8MPa | 1.0MPa | 1.25MPa | 1.6MPa | 2.0MPa | ||||||
壁厚 | 重量 | 壁厚 | 重量 | 壁厚 | 重量 | 壁厚 | 重量 | 壁厚 | 重量 | 壁厚 | 重量 | |
mm | mm | Kg/m | mm | Kg/m | mm | Kg/m | mm | Kg/m | mm | Kg/m | mm | Kg/m |
65 |
|
|
|
|
|
|
|
| 8 | 1.35 | 9 | 1.50 |
96 |
|
|
|
|
|
|
|
| 9 | 2.33 | 10 | 2.55 |
110 |
|
|
|
|
|
|
|
| 8 | 2.42 | 10 | 2.97 |
130 |
|
|
|
|
|
| 8 | 2.90 | 10 | 3.56 | 12 | 4.21 |
159 |
|
|
|
|
|
| 10 | 4.43 | 12 | 5.24 | 15 | 6.42 |
168 |
|
|
|
| 8 | 3.8 | 10 | 4.69 | 13 | 5.98 | 16 | 7.22 |
205 |
|
| 8 | 4.68 | 10 | 5.79 | 12 | 6.88 | 15 | 8.46 | 18 | 10.00 |
219 |
|
| 9 | 5.61 | 11 | 6.80 | 13 | 7.95 | 16 | 9.65 | 20 | 11.82 |
236 |
|
| 10 | 6.71 | 12 | 7.98 | 14 | 9.23 | 18 | 11.65 | 22 | 13.98 |
250 |
|
| 10 | 7.13 | 12 | 8.48 | 15 | 10.47 | 19 | 13.04 | 23 | 15.51 |
273 | 9 | 7.06 | 11 | 8.56 | 13 | 10.04 | 16 | 12.21 | 21 | 15.72 | 25 | 18.41 |
280 | 9 | 7.24 | 11 | 8.79 | 14 | 11.06 | 17 | 13.28 | 21 | 16.15 | 26 | 19.61 |
300 | 10 | 8.61 | 12 | 10.26 | 15 | 12.70 | 18 | 15.08 | 23 | 18.92 | 27 | 21.89 |
315 | 10 | 9.06 | 12 | 10.80 | 15 | 13.37 | 19 | 16.70 | 24 | 20.74 | 29 | 24.63 |
325 | 10 | 9.36 | 13 | 12.05 | 16 | 14.68 | 19 | 17.27 | 24 | 21.46 | 30 | 26.28 |
350 | 11 | 11.08 | 14 | 13.97 | 17 | 16.80 | 21 | 20.52 | 26 | 25.02 | 32 | 30.22 |
377 | 12 | 13.01 | 15 | 16.13 | 18 | 19.19 | 22 | 23.20 | 28 | 29.02 | 35 | 35.55 |
400 | 12 | 13.83 | 16 | 18.25 | 19 | 21.50 | 24 | 26.80 | 30 | 32.97 | 36 | 38.92 |
415 | 13 | 15.52 | 16 | 18.96 | 20 | 23.46 | 25 | 28.96 | 31 | 35.35 |
|
|
426 | 13 | 15.95 | 17 | 20.65 | 20 | 24.12 | 25 | 29.77 | 32 | 37.45 |
|
|
536 | 16 | 24.71 | 21 | 32.12 | 26 | 39.38 | 32 | 47.90 |
|
|
|
|
560 | 16 | 25.85 | 22 | 35.15 | 27 | 42.74 | 33 | 51.65 |
|
|
|
|
630 | 19 | 34.48 | 25 | 44.92 | 30 | 53.46 | 37 | 65.16 |
|
|
|
|
652 | 20 | 37.54 | 26 | 48.34 | 32 | 58.92 | 38 | 69.30 |
|
|
|
|
710 | 21 | 42.93 | 27 | 54.77 | 34 | 68.26 |
|
|
|
|
|
|
800 | 23 | 53.08 | 31 | 70.08 | 38 | 86 |
|
|
|
|
|
|